Reason for stainless steel water tank leakage
Stainless steel tank leakage and rusty In fact, there are many reasons for this problem. You know what the number of manufacturers doing jerry-building, cheat for the activities, perhaps you spend a large cost in exchange for only 201 material, or 304 material, in fact, should really use 3042 / B, more resistant to corrosion 316L, 444, and so on. My specific analysis is as follows:
One: with the welding technology, with the welding material.
Two: with the thickness of the plate, and now some manufacturers, offer very low, mainly thinning thin plate.
Three: silk material, generally contact with the water must use stainless steel, but some wire, the flange is actually iron. As long as the material is not right, it is easy to rust out, undeniable. Also hope that we can not seek, can not seek cheap, no manufacturers are not the pursuit of profit, offer too much too much, then there are problems. But also a very high price, but also to buy bad goods, where reported to sympathy. Really, stainless steel 200 series sheet and 300 series plate is difficult to identify the naked eye. Please also pay attention to a lot of product warranty. When using stainless steel water tank, do not apply excessive load to piping inlet and outlet. Do not apply the weight of the valve and the large diameter pipe directly to the tank outlet, if necessary, set the pipe support: the expansion of the pipe, shrinkage, vibration must be installed flexible flexible joints.
In response to this situation, how should we respond to the following Hebei LongTime water tank Company for us to explain the phenomenon of water leakage for the tank, our response.
1: election on the manufacturers
It is recommended to choose a formal business, so as to be able to ensure the quality of the tank to avoid the trouble of water tank leakage.
Second: the tank repair method
(1) with tin zinc aluminum alloy welding aluminum tank
Will be 6o% of tin, 35% of the zinc and 5% of the aluminum iron spoon and other items in the heating and melting, cast into a thin electrode. Cleaning the crack at the oil, with an abrasive cloth polished oxide film, and then a screwdriver or broken blade scraping clean, with a torch to aluminum heating to 300 ℃ -40o ℃ (note the temperature can not be too high), the electrode rubbed in the crack When the electrode melts, use a screwdriver to rub the molten alloy alloy at the crack, so that the alloy flows into the crack, and then gradually thicken the solder layer.
(2) with adhesive penetration method to repair the tank crack
The water tank to dry, drilling at both ends of the hole 3 mm hole, such as the crack is long or curved, can be in the middle or corner and then drill a hole, with broken strip scraping crack, revealing metallic luster. With 502 adhesive drops in two holes, with 3 mm aluminum rivet riveting, closed crack. The adhesive drops in the crack, and then use the hammer in the cracks in the two measured percussion, the adhesive into the cracks, every 30 minutes and then drop the adhesive and knock, repeat 2 times -4 times, until the glue can not penetrate, put 3 hours - 5 hours to use.
Above is the stainless steel water tank leakage, our response measures, I believe we will certainly be helpful to see, as long as our water tank there is a little leak, we can according to the above measures to solve. If you still have questions about water tank, please contact us on E-mail: rask@coolingtowerfiller.com, or you can also contact us on whats app: 008618330029204, looking forward to your reply.